When choosing stone coated roofing tile, many people have a misconception that the thicker the steel plate, the better the stone coated roofing tile. Actually, this is a misconception among many people. Today, we will explain to you the key factors that determine the lifespan of stone coated roofing tile, so that you can have a more scientific and comprehensive understanding of stone coated roofing tile.
Firstly, we must clarify that among the many factors that affect the lifespan of stone coated roofing tile, the thickness of the aluminum zinc coating plays a more critical role compared to the thickness of the steel plate. The aluminum zinc coating is the first line of defense for stone coated roofing tile to resist external environmental erosion, and its importance cannot be underestimated.
The aluminum zinc coating has excellent corrosion resistance. It can effectively block the erosion of steel plates by rainwater, air, and various chemicals, whether it is acid rain corrosion, high salt air erosion in coastal areas, or chemical pollution in industrial areas. Aluminum zinc coating can provide reliable protection for steel plates. In some buildings that have been exposed to harsh weather conditions or high pollution areas for a long time, the characteristic of aluminum zinc coating is particularly important. For example, in a seaside resort hotel, the sea breeze carries a large amount of salt, and ordinary steel plates are prone to rusting and corrosion. However, stone coated roofing tile with sufficient thickness of aluminum zinc coating can remain intact for a long time, greatly extending the service life of the roof.
On the other hand, although thick steel plates may give people a stronger and more sturdy feeling to some extent, in reality, simply increasing the thickness of steel plates after meeting the basic structural strength requirements does not have a significant effect on improving the overall life of stone coated roofing tile. Moreover, excessively thick steel plates can increase the weight of stone coated roofing tile, which not only puts greater pressure on the load-bearing structure of the roof and increases construction costs, but also brings many inconveniences during transportation and installation, leading to an increase in labor costs.
From the perspective of production technology, the quality and thickness control of aluminum zinc coating are more complex and critical. The high-quality aluminum zinc plating process requires advanced equipment and strict technical standards to ensure that the aluminum zinc plating layer adheres uniformly and firmly to the surface of the steel plate. This process involves precise control of temperature, time, plating solution composition, and other aspects. Any deviation in any link may affect the performance of the aluminum zinc coating, thereby affecting the service life of the colored stone metal tile. The control of steel plate thickness is relatively simple, and it is not difficult to achieve a certain thickness accuracy under modern steel processing technology.
In addition, the lifespan of stone coated roofing tile is also influenced by a combination of other factors. For example, the quality and adhesion of surface colored sand can provide good decorative effects and certain protective effects. High quality colored sand has strong adhesion with steel plates and aluminum zinc plating layers, which can effectively prevent colored sand from falling off and maintain the beauty and integrity of the tile surface; There is also the performance of sealing materials. Good sealing materials can prevent rainwater leakage and avoid problems such as rusting of steel plates caused by leakage; The rationality of installation technology cannot be ignored. Proper installation can ensure the stability of stone coated roofing tile on the roof and reduce the risk of damage caused by improper installation.
So, stone coated roofing tile are not necessarily better with thicker steel plates, the thickness of the aluminum zinc coating is more important in determining their lifespan. When choosing stone coated roofing tile, we should not only focus on the thickness of the steel plate, but also consider multiple factors such as the thickness of the aluminum zinc layer, the quality of the colored sand, the performance of the sealing material, and the installation process. As a professional colored stone metal tile enterprise SKW, we are committed to optimizing various production processes and strictly controlling product quality to provide high-quality and long-lasting colored stone metal tile products to global customers, meeting the needs of different construction projects and finding the perfect balance between aesthetics and durability for your building roof.